Equivalence:Lewatit M510,Dowex SBR-P,Purolite A400,ResinTech SBG1P,Amberlite IR402, Tulsion A2
Equivalence:Lewatit M510,Dowex SBR-P,Purolite A400,ResinTech SBG1P,Amberlite IR402, Tulsion A23P
201x4 is a Gel Type Strong Base Anion Exchange Resin based on polystyrene matrix with quaternary ammonium functional group. 201x4 gives high throughput and consistent quality. 201x4 resins in combination with 001x7 resins, gives excellent performance in mixed beds.
201x4 is high capacity resin which achieves lowest possible silica under varied water conditions. The resin is supplied in transparent moist bead form with high beads strength. The resin is suitable for demineralization system incorporating co-current and counter-current operations.
PROPERTIES | |
Matrix | Cross linked polystyrene |
Functional Group | Quaternary Ammonium |
Ionic Form | Cl- Chloride |
Physical Form | Hard moist beads |
Particle size (mm) | 0.315-1.25 |
Moisture content % | 50-60 |
Total Exchange Capacity (Min) eq/ltr | 1.1 |
Bulk density or shipping weight gms/ltr | 660-710 |
Operating pH range | 0-14 |
Solubility in common solvents | Insoluble |
Operating Temperature℃ (max) | 80 |
Volume change% (max):Cl- to OH- | 25 |
SUGGESTED OPERATING CONDITIONS | ||
Bed Depth | Meter | 1.0-3.0 |
Regenerant Concentration | % | 4-5 NaOH |
Regenerant Flow Rate | Meter/Hour | 4-6 |
Regenerant Contact Time | Minutes | 30-60 |
Regeneration Level 100% | Kgs/m3 of resins | 40-80 NaOH |
Rinse Flow Rate | Meter/Hour | 15-25 |
Rinse Time | Minutes | 25 |
Running Flow Rate | Meter/Hour | 15-25 |
APPLICATIONS: 201x4 is recommended in the two bed system of demineralization system. The resin has a lower silica and carbonic acid leakages, hence gives higher silica removal capacity in demineralization units.
201x4 is also used as a mixed bed resin along with 001x7 as a polishing unit to achieve lowest residual silica in treated water and water of high purity is obtained. The resin is also used in absorption process, fractionalization process of weak acid, biochemical’s and pharmaceutical intermediates.201x4 and 201x7 are quite similar, the difference between them is the degree of porosity. 201x4 has greater porosity that gives it faster kinetics, and greater ability to reversibly sorb slow moving ions such as Naturally occurring Organic Matter (NOM). At lower regeneration levels and where chlorides make up a substantial portion of the anion load, or where the removal and elution of naturally occurring organics is of concern 201x4,202 should be considered. At the higher regeneration levels used in mixed bed polishers 201x7 provides higher capacity, and the lowest possible TOC leach rates.
PACKING:
Super Sack | 1000Liters |
PP/PE Bag | 25Liters |
PP/PE Bag | 25Kgs |
CAUTION: Strong oxidizing agents like nitric acid can cause explosive type reaction, when mixed with Ion Exchange resins. Knowledgeable sources should be consulted in the handling of this material.
NOTE: Ion Exchange Resins are sold on a volume basis, but are packed and shipped by weight. The shipping weight for each resin is fixed & does not take into consideration the variations in density and moisture content allowed within the product specifications. Therefore although the weight of the material is constant, there may be slight variations in volume, reflecting batch to batch variation of density and moisture content.
STORAGE CONDITIONS: The resin supplied in drums or bags should be stored in cool shed (warehouse) away from direct sunlight & should be periodically damped down with clean water.